HOAT - Blend Tech Automotive Inorganic
HOAT additive syrup is a single component product that is used to blend premium quality extended life antifreeze / engine coolant for use in virtually any vehicle. Used as directed, blending HOAT with glycol* or 50% glycol and water will result in engine coolant that complies with ASTM D3306 (virgin), ASTM D6471 / 6472 (recycled), ASTM D6210 and TMC RP-329 (EG) RP-330 (PG). The chemistry is compatible with Valvoline G-05 (Mercedes Ford & Chrysler factory fill), Fleetguard ES Compleat and other hybrid technology coolants. This type of coolant is sometimes referred to as “heavy duty extended life”, “global extended service” or “HOAT”.
HOAT Blending Syrup if used a s directed will provide satisfactory performance in most cars and trucks including the following:
| ASTM D-6210 | Mack Trucks |
|---|---|
| ASTM D-3306 | CNH |
| US Military CID AA52624A | Thermo-King |
| Chrysler (all) | Intemational Truck & Engine Company |
| Cummins Engine | Volvo Trucks |
| Detroit Diesel Corp (93K217) | Freightliner |
| Ford Motor Co. (all) | Mercedes (all) John Deere (all) |
| Caterpillar (DEAC type) |
Table of properties and Typical ASTM Test Results blended with EG as Antifreeze
| Test / Property | Method | Result |
|---|---|---|
| Color | Visual | Yellow |
| Relative Density (Specific Gravity) | ASTM D1122 | 1.123 |
| Freeze Point @ 50% in water | D 1177 | -38 F (-39 C) |
| Boiling Point (neat) | ASTM D1120 | 338 F (169 C) |
| Boiling Point 50% in water | ASTM D1120 | 226 F (108 C) |
| PH 50% (in water) | ASTM D1287 | 10.8 |
| Effect on Auto Finish | ASTM D 1882 | No effect |
| Chloride | ASTM D3634 | 9 ppm |
| Water Content | ASTM D1123 | 3.1% |
| Reserve Alkalinity | ASTM D1121 | 5.9 |
| Foaming Tendencies | ASTM D1881 | 50 ml / 1.6 sec. Break time |
| Silicate as Si | ASTM D6130 | 250 |
| Nitrite (NO) | ASTM D5827 | 2600 |
| Molybdate (Mo04) | ASTM D5827 | <1 |
| Phosphate as P | ASTM D6130 | <1 |
| Sebacic acid | HPLC | 800 |
| Corrosion of heat reflecting aluminum surface | ASTM D4340 | 0.01 mg/cm2/week |
| Cavitation / Erosion-Corrosion of Aluminum Water Pump | ASTM D2809 | 9 |
| Corrosion in Glassware | ASTM D1384 | Copper 3 mg Solder 1 mg Brass 2 mg Steel 2 mg Cast Iron 2 mg Cast Aluminum -2 mg |
| Simulated Service | ASTM D2570 | Copper 3 mg Solder 5 mg Brass 3 mg Steel 2 mg Cast Iron D Cast Aluminum 1 mg |
| Glycol % | ASTM E202 | 96.0% min |
| Military Compatibility | Pass | |
| Military Storage Stability | Pass |
Specifications
CAS Number
64-19-7
Grade
Technical
Shipping
Ships in 1-2 Business Days
Appearance
liquid
Density
1.069 g/cm3
Evaporation Rate
1
Flash Point
56 - 71 °C (133 - 160 °F)
Odor
vinegar-like
pH
2.4 @ 20 - 25 °C (68 - 77 °F)
Recommended Use
Acid.
Relative Vapor Density
> 1